Compositions comprising functionalized polyphenylene ether resins

ABSTRACT

The invention relates to a method of forming a polyphenylene ether resin containing residual aliphatic unsaturation. A polyphenylene ether is reacted with a capping agent in a solvent to form the polyphenylene ether resin containing residual aliphatic unsaturation, which is precipitated from solution by combining the solution with an antisolvent. The precipitated polyphenylene ether resin containing residual aliphatic unsaturation has lower levels of residual impurities than the same compound isolated by devolatilization.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of U.S. application Ser. No. 10/063,152 filed Mar. 26, 2002 now U.S. Pat. No. 6,627,708, which is a division of U.S. application Ser. No. 09/683,352 filed 18 Dec. 2001 (now U.S. Pat. No. 6,469,124), which is a division of U.S. application Ser. No. 09/613,112 filed 10 Jul. 2000 (now U.S. Pat. No. 6,384,176).

BACKGROUND OF INVENTION

Polyphenylene ether resins (hereinafter “PPE”) are commercially attractive materials because of their unique combination of physical, chemical, and electrical properties. Furthermore, the combination of PPE with other resins provides blends that result in additional overall properties such as chemical resistance, high strength, and high flow.

One technical obstacle to the development of such blends is the lack of compatibility between PPE and many resins. This lack of compatibility manifests itself often through very poor physical properties as well as delamination in molded parts. Methods have been developed to improve the PPE compatibility with many resins such as, for example, with polyesters and polyamides. One of the more effective methods involves functionalizing PPE to make functionalized PPE containing moieties such as acid, anhydride, epoxy, orthoester, and the like that are reactive with the other resin in the blend. It is believed that when the functionalized PPE is allowed to react with the other resin that relatively small amounts of copolymer between the resins are formed. The copolymer is believed to be in large part responsible for improved compatibility between the PPE and the other resin. Indications of improved compatibility include resistance to delamination, improved physical properties such as increased tensile and impact properties and a stabilized morphology between the blend component phases under static and/or low shear conditions.

Methods to prepare functionalized PPE have included solution functionalization with an acid halide containing compound, such as trimellitic anhydride acid chloride, to make an endcapped PPE containing at least one reactive moiety such as acid, anhydride, epoxy, orthoester, and the like. This method is rather limited in the variety of functionalized PPE that can be made. Also, the by-products from the capping reaction tend to cause emulsion and/or isolation issues in the solvent precipitation stage of the process.

Another known method to prepare functionalized PPE related to melt functionalization of the PPE in an extruder. This method involved melting and mixing PPE with a functionalizing agent to result in a functionalized PPE. The functionalizing agent is typically a compound containing a carbon-carbon double or triple bond and one of the aforementioned reactive moieties and is believed to react through the unsaturated bond to functionalize the PPE. Additional polymers could be fed into the same extruder or alternatively, the functionalized PPE could be isolated and subsequently used to prepare other compositions. Melt functionalization has issues, such as difficulty in feeding PPE into the extruder due to low bulk density and wide particle size distribution. Moreover, PPE are often powders and require special handling to avoid potential dust explosion.

As explained above, the methods known in the art teach functionalization of the PPE with reactive groups such as acid, anhydride, epoxy, orthoester, and the like. However, for blending PPE with resin systems that involve curing or polymerization reactions, including radical reactions, it would be highly desirable to have a PPE that contained residual aliphatic unsaturation and capped phenolic end groups at the same time. Incorporation of unsaturated species onto the PPE to result in an olefinic functionalized PPE may allow for chemical grafting to occur between the olefinic functionalized PPE and the other unsaturated species that are being polymerized. Moreover, the hydroxyl groups that exist on PPE may interfere with radical polymerization reactions of unsaturated monomers and lead to undesirable low polymerization rates of the unsaturated monomer species.

PPE known in the art typically are of fairly high molecular weight for blending in the melt phase with other polymers and generally have in excess of 50 repeat monomer units, most often in excess of 80 or more repeat monomer units. Consequently, functionalization reactions and isolation methods have been developed for high molecular weight PPE. Although many physical properties, such as tensile properties, are enhanced with the high molecular weight of the PPE in the polymeric blend, in other new resin blend compositions, such as, for example, the polymerization of vinyl-substituted aromatic monomers, the high viscosity of the PPE having more than 50 repeat monomer units is undesirable as it presents difficulty with mixing. Additionally, the overall number of available endgroups available for chemical modification becomes fairly limited as the molecular weight increases.

For blending PPE with resin systems that involve curing or polymerization reactions, including radical reactions, it would be highly desirable from the standpoints of low viscosity for mixing and a high endgroup number for functionalization to have a PPE that contained residual aliphatic unsaturation and that has less than 50 repeat monomer units on average, preferably less than about 35 repeat monomer units on average. It is therefore apparent that a need continues to exist for novel and improved methods to prepare functionalized PPE containing residual aliphatic unsaturation, especially low molecular weight PPE (i.e. PPE having an intrinsic viscosity less than about 0.30 dl/g as measured in chloroform at 30° C.).

SUMMARY OF INVENTION

The needs discussed above have been generally satisfied by the discovery of a process for preparing functionalized PPE containing aliphatic unsaturation. In one embodiment, the process comprises oxidative coupling in a reaction solution at least one monovalent phenol species using an oxygen containing gas and a complex metal catalyst to produce a PPE; and functionalizing the PPE, preferably prior to and/or during at least one isolation step for devolatilization of the reaction solvent, with an unsaturated compound of the formula (I):

wherein R¹ is an aliphatic or aromatic residue, for example, —CH₂— but may be multiple —CH₂— groups, e.g., n can vary from 1 to about 10 or more, or alternatively, n may equal zero wherein the formula is an acrylic residue, and wherein each of R², R³, and R⁴ are independently hydrogen, alkyl, or aryl, and wherein X is a residue of one of the following formulae (II):

or wherein X is a halogen or a residue of the formula (III):

wherein R⁷ is an aliphatic or aromatic residue, for example, —CH₂— but may be multiple —CH₂— groups, e.g., m can vary from 1 to about 10 or more, or alternatively, m may equal zero (wherein if n and m both equal zero, the unsaturated compound is an acrylic anhydride), and wherein each R⁸, R⁹, and R¹⁰ are independently hydrogen, alkyl, or aryl. In a preferred embodiment, the unsaturated compound is of the formula (IV):

wherein each of n, R¹, R², R³, and R⁴ are as previously described. In an especially preferred embodiment, the unsaturated compound is of the formula (V):

Another embodiment is a process to prepare a polyphenylene ether resin containing aliphatic unsaturation, comprising: reacting a polyphenylene ether resin with an unsaturated compound in a solvent to form a solution containing a polyphenylene ether resin containing aliphatic unsaturation, wherein the unsaturated compound has the formula

wherein R¹ is an aliphatic or aromatic residue, n can vary from 0 to about 10, and wherein each of R², R³, and R⁴ are independently hydrogen, alkyl, or aryl, and wherein X is a residue of one of the formulae

wherein R⁷ is an aliphatic or aromatic residue, m can vary from 0 to about 10, and wherein each R⁸, R⁹, and R¹⁰ are independently hydrogen, alkyl, or aryl; and precipitating the polyphenylene ether containing aliphatic unsaturation from the solution by combining the solution with an antisolvent, wherein the antisolvent comprises a compound selected from water, alkanols having one to about ten carbon atoms, ketones having three to about ten carbon atoms, and alkanes having five to about ten carbon atoms, and mixtures thereof.

The description that follows provides further details regarding various embodiments of the invention.

DETAILED DESCRIPTION

One embodiment of this invention provides for a process for the preparation of functionalized PPE containing aliphatic unsaturation, preferably having an intrinsic viscosity between about 0.08 dl/g and 0.60 dl/g, more preferably between about 0.10 dl/g and about 0.30 dl/g, by oxidative coupling at least one monovalent phenol species, preferably at least a portion of which have substitution in at least the two ortho positions and hydrogen or halogen in the para position, using an oxygen containing gas and a complex metal-amine catalyst, preferably a copper (I)-amine catalyst, as the oxidizing agent and, preferably extracting at least a portion of the metal catalyst as a metal-organic acid salt with an aqueous containing solution, and functionalizing the PPE with the addition of at least one unsaturated anhydride of the formula (I) prior to and/or during at least one isolation step for removal of the reaction solvent. In one embodiment, the functionalization is at least partly done in a flash process to concentrate the PPE reaction solution. In another embodiment, the functionalization is at least partly done prior to a flash process to concentrate the PPE reaction solution. In yet another embodiment, the functionalization is at least partly done in a devolatilizing extruder. The functionalization reaction is preferably done in the presence of at least one catalyst, preferably an amine-type catalyst. These and other embodiments will become apparent in the description that follows.

The PPE employed in the present invention are known polymers comprising a plurality of structural units of the formula (VI):

wherein each structural unit may be the same or different, and in each structural unit, each Q¹ is independently halogen, primary or secondary lower alkyl (i.e., alkyl containing up to 7 carbon atoms), phenyl, haloalkyl, aminoalkyl, hydrocarbonoxy, or halohydrocarbonoxy wherein at least two carbon atoms separate the halogen and oxygen atoms; and each Q² is independently hydrogen, halogen, primary or secondary lower alkyl, phenyl, haloalkyl, hydrocarbonoxy or halohydrocarbonoxy as defined for Q¹. Most often, each Q¹ is alkyl or phenyl, especially C₁₋₄ alkyl, and each Q² is hydrogen.

Both homopolymer and copolymer PPE are included. The preferred homopolymers are those containing 2,6-dimethyl-1,4-phenylene ether units. Suitable copolymers include random copolymers containing such units in combination with (for example) 2,3,6-trimethyl-1,4-phenylene ether units. Also included are PPE containing moieties prepared by grafting vinyl monomers or polymers such as polystyrenes and elastomers, as well as coupled PPE in which coupling agents such as low molecular weight polycarbonates, quinones, heterocycles and formals undergo reaction in known manner with the hydroxy groups of two poly(phenylene ether) chains to produce a higher molecular weight polymer, provided a substantial proportion of free OH groups remains.

The molecular weight and intrinsic viscosity of the PPE can vary widely, depending at least in part on the intended end-use for the PPE. The intrinsic viscosity (hereinafter “I.V.”) of the PPE is most often in the range of about 0.08-0.60 dl./g., preferably in the range of about 0.10-0.49 dl./g., more preferably in the range of about 0.10-0.30 dl./g., as measured in chloroform at 25° C. In one especially preferred embodiment, the PPE has an I.V. in the range of about 0.10-0.25 dl./g. One unexpected aspect of the process is the ability to utilize a very wide range of I.V.

The PPE are typically prepared by the oxidative coupling of at least one monohydroxyaromatic compound such as 2,6-xylenol, 2,3,6-trimethylphenol, or mixtures of the foregoing by methods known in the art. Catalyst systems are generally employed for such coupling and they typically contain at least one heavy metal compound such as a copper, manganese, or cobalt compound, usually in combination with various other materials.

It will be apparent to those skilled in the art from the foregoing that the PPE contemplated in the present invention include all those presently known, irrespective of variations in structural units or ancillary chemical features.

The functionalizing agents used in the present invention to introduce the aliphatic unsaturation onto the PPE are unsaturated compounds of the formula (I):

wherein R¹ is an aliphatic or aromatic residue, for example, —CH₂— but may be multiple —CH₂— groups, e.g., n can vary from 1 to about 10 or more, or alternatively, n may equal zero wherein the formula is an acrylic residue, and wherein each of R², R³, and R⁴ are independently hydrogen, alkyl, or aryl, and wherein X is a residue of one of the following formulae (II):

alternatively, X may be a halogen or may be a residue of the formula (III):

wherein R⁷ is an aliphatic or aromatic residue, for example, —CH₂— but may be multiple —CH₂— groups, e.g., m can vary from 1 to about 10 or more, or alternatively, m may equal zero (wherein if n and m both equal zero, the unsaturated compound is an acrylic anhydride), and wherein each R⁸, R⁹, and R¹⁰ are independently hydrogen, alkyl, or aryl. In a preferred embodiment, the unsaturated compound is of the formula (IV):

wherein each of n, R¹, R², R³, and R⁴ are as previously described. In an especially preferred embodiment, the unsaturated compound is of the formula (V):

However, included within the scope of the present invention are “mixed” or “unsymmetrical” anhydrides of formula (IV).

Although not wishing to be bound by any theory on the nature or mechanism of the chemical reaction between the PPE and the unsaturated compound of formula (I), it is presumed that the functionalization of the PPE takes place through the hydroxyl groups on the PPE resulting in a PPE containing aliphatic unsaturation comprising the formula (VII):

each of Q¹, Q², n, R¹, R², R³, and R⁴ is as previously defined and j comprises a range of values generally on average between about 10 and 110 depending in large part on the I.V. of the PPE. In one embodiment, j has an average value less than 49. In another embodiment, j has an average value less than 34. In a preferred embodiment, the PPE containing aliphatic unsaturation comprises the formula (VIII):

each of n, j, R¹, R², R³, and R⁴ is as previously defined. In an especially preferred embodiment, n is zero, R² is CH₃ or hydrogen and both of R³ and R⁴ are hydrogen. There can also be multiple aliphatic unsaturation introduced onto the PPE through incorporation of branching agents and/or coupling agents into the PPE backbone structure such that more than one end of the PPE contains hydroxyl groups for capping. Such branching agents and/or coupling agents are known in the art and include compounds such as, for example, tetramethylhydroquinone and trishydroxyphenol.

The functionalization reaction is preferably performed in a solvent, preferably in the polymerization reaction solvent. Suitable solvents are disclosed in the above-noted Hay patents. Aromatic solvents such as benzene, toluene, ethylbenzene, xylene, and o-dichlorobenzene are especially preferred, although tetrachloromethane, trichloromethane, dichloromethane, 1,2-dichloroethane and trichloroethylene may also be used.

One unexpected advantage of the present process when used to make functionalized low I.V. PPE is that a higher solids loading is possible as compared to processes that make higher (i.e. >0.28 I.V.) PPE. Without the increased solution viscosity build that concomitantly accompanies high molecular weight polymer, the final solids concentration can be increased by at least 20%, with increases of 30% or more possible. Thus, the present process affords a method for increased reactor utilization and productivity without increasing the size or number of the reactor vessels.

The temperature to carry out the functionalization stage of the invention generally ranges from about 20° C. to about 100° C., although higher temperatures are also possible. More preferably, the temperature range is from about 45° C. to about 80° C. At substantially higher temperatures, side reactions can occur leading to reaction by-products. One unexpected advantage of the present process is the relatively low temperatures that can be utilized and still achieve high levels of functionalization at acceptable reaction times.

After removal of the catalyst, the PPE containing solution is concentrated to a higher solids level as part of the isolation of the PPE. It was unexpectedly found that PPE can be readily functionalized to a PPE containing aliphatic unsaturation prior to and/or during this solvent removal process by addition of at least one functionalizing agent of the formula (I). The location of the addition of the at least one functionalizing agent will depend on several factors such as the stability of the agent, the volatility of the agent to the isolation conditions, the flexibility of the equipment for addition points, and the like. For functionalizing agents that are volatile in the isolation process, addition of the functionalizing agent prior to solvent removal is often preferred so as not to remove the functionalizing agent before it has functionalized the PPE. For less volatile functionalizing agents, greater flexibility in the location of the addition is possible. It is also possible to add functionalizing agent at several points during the process.

The amount of the above mentioned functionalizing agents that is required to appropriately functionalize the PPE is that which is sufficient to improve the compatibility between the various components in the final composition, i.e. between the PPE and the other resins and composite formulations, e.g., unsaturated polyesters, acrylics, and thermoplastics such as polyolefins. As previously discussed, indications of improved compatibility include resistance to delamination, improved physical properties such as increased tensile and impact properties and a stabilized morphology between the blend component phases under static or low shear conditions. For the most part, it is desirable for all hydroxy end groups on the PPE to be capped by the method of this invention. However, the invention includes compositions which contain a proportion of uncapped PPE; that is, PPE containing terminal hydroxy groups.

An effective amount of the above mentioned unsaturated compounds, based on the amount of the PPE, is generally up to about 3 molar equivalents, and is preferably up to about 2 molar equivalents, most preferably up to about 1.2 molar equivalents, all based upon the amount of terminal hydroxyl groups on the PPE as determined by FT-IR, usually in carbon disulfide. The actual amount utilized will also depend on, for example, the reactivity of the unsaturated functionalizing agent with the PPE hydroxyl groups, the catalyst employed, the reaction conditions, and the degree of capping that is desired in the PPE.

The capping efficiency and rate are improved by the addition of at least one catalyst. Although a wide variety of catalysts are useful, a particularly useful group of catalysts include the tertiary amines. It was unexpectedly found that 4-dialkylaminopyridines, such as 4-dimethylaminopyridine, as well as 4-pyrrolidinopyridine are especially useful for achieving high conversions at short reaction times under mild conditions as compared to other tertiary amines. The amount of catalyst can vary widely, however, the amount is generally an amount effective to improve the degree of conversion under a given set of reaction conditions as compared to the degree of conversion under the same conditions without the catalyst. Useful amounts generally range from about 0.1% by weight to about 10% by weight, preferably from about 0.5% by weight to about 5% by weight based on the amount of the PPE. An exact amount can be readily determined by statistical analysis under the reaction conditions, including the actual functionalizing agent reactivity, the reaction conditions, the equipment available, and the like without undue experimentation.

The functionalized PPE may be isolated in a variety of ways, including precipitation methods and total isolation methods. A total isolation process is often preferred for isolating the functionalized PPE when the I.V. is less than about 0.25 dl/g as measured in chloroform at 25° C. As part of the total isolation, a portion of the solvent is preferably removed in order to reduce the solvent load on the total isolation equipment. Concentration of the PPE containing solution is preferably accomplished by reducing the pressure in a solvent flash vessel while preferably increasing the temperature of the PPE containing solution. Pressures of about 35 to 50 bar are desirable with solution temperatures increased to at least 200° C., preferably of at least 230° C. A solids level of PPE of at least 55%, preferably of at least 65% or higher is desirable.

The unsaturated functionalizing agent can be effectively added to the PPE at several locations during the isolation process. For example, functionalizing agent may be added prior to removal of solvent, the functionalizing agent may be added during the concentration of the reaction mixture, or both. Likewise, functionalizing agent can be added with the concentrated reaction solution into the final devise for solvent removal. Functionalizing agent may alternatively be added simultaneously at several different locations. The selection of the addition location may be dictated by the actual equipment utilized and by the properties of functionalizing agent with a determination of an optimum location.

For total isolation processes, the final isolation of the functionalized PPE is preferably carried out in a devolatilizing extruder although other methods involving spray drying, wiped film evaporators, flake evaporators, and flash vessels with melt pumps, including various combinations involving these methods are also useful and in some instances preferred. As previously described, total isolation is preferable from the viewpoint that oligomeric species are not removed to the same degree as with precipitation. Likewise, isolation yields are extremely high and are near quantitative. In these techniques it is highly preferred that the PPE polymerization catalyst (i.e. metal catalyst) removal be completed in the prior process steps as any metal catalyst remaining in solution will necessarily be isolated in the PPE.

Devolatilizing extruders and processes are known in the art and typically involve a twin-screw extruder equipped with multiple venting sections for solvent removal. The devolatilizing extruders most often contain screws with numerous types of elements adapted for such operations as simple feeding, devolatilization and liquid seal formation. These elements include forward-flighted screw elements designed for simple transport, and reverse-flighted screw and cylindrical elements to provide intensive mixing and/or create a seal. Particularly useful are counterrotating, non-intermeshing twin screw extruders, in which one screw is usually longer than the other to facilitate efficient flow through the die of the material being extruded. Such equipment is available from various manufacturers including Welding Engineers, Inc.

In the practice of one embodiment of the present invention, the preheated concentrated solution containing the functionalized PPE is fed into the devolatilizing extruder and maintained at a temperature less than about 300° C., and preferably less than about 275° C., with pressures in the vacuum vent of less than about 1 bar. The exact temperature will depend in large part on the I.V. of the functionalized PPE and the corresponding viscosity associated with that I.V. resin. It is noted that the functionalizing agent may alternatively be added at various locations along the length of the extruder with good results. The resultant solvent level is preferably reduced to less than about 1200 ppm, preferably less than about 600 ppm, and most preferably less than about 400 ppm.

Another unexpected result obtained through the use of a devolatilizing extruder was the extremely high yield of PPE achieved in the process. For example, a PPE yield of over 99% was obtained even for PPE having a low I.V. (typically on the order of about 0.08 dl/g to about 0.25 dl/g) whereas in the precipitation process known in the art, the yield of similar low I.V. PPE was less than 90%. Thus, the present process comprising a devolatilizing extruder affords a method to prepare functionalized low molecular weight polyphenylene ether resin containing aliphatic unsaturation, typically within the intrinsic viscosity range of about 0.08 dl/g to about 0.25 dl/g, in a yield of over 90%, preferably over 95%, more preferably over 98% and most preferably over 99%, based upon the amount of monovalent phenol utilized in the oxidative coupling.

When using a devolatilization extruder for the total isolation of the low I.V. functionalized PPE as previous described, it was found that traditional underwater or water spray cooling of strands of extrudate followed by chopping the extrudate into pellets gave unacceptable results presumably due to the low melt strength and inherent brittle nature of low I.V. PPE. It was found that special pelletization techniques can overcome these difficulties. Useful techniques include die-face pelletization, including underwater pelletization and flaking, declining angle strand pelletization using water spraying, and vibration drop pelletization with underwater pelletization especially suitable.

The collected PPE pellets can be dried using techniques standard in the art including centrifugal dryers, batch or continuous oven dryers, fluid beds, and the like. Determination of an appropriate set of conditions can be readily determined by one of skill in the art without undue experimentation.

As an alternative to completely isolating the functionalized PPE, one or more resins may be added to the devolatilized functionalized PPE in the same process. The one or more resins may be fed into the devolatilizing extruder although additional extruders may also be used. Possible variations include melt feeding the one or more resins into the devolatilizing extruder or melt feeding the functionalized PPE from the devolatilizing extruder into a second compounding extruder as well as combinations of these. Accordingly, in one embodiment a compatibilized blend is afforded by the process without complete isolation of the functionalized PPE. The one or more resins can vary widely and can also include additives common to such compatibilized blends. Such additives include impact modifiers, lubricants, flame retardants, pigments, colorants, fillers, reinforcing agents, carbon fibers and fibrils, and the like. Preferred resins include polyamides, polyesters, polyarylene sulfides, polycarbonates, polyetherimides, polyarylenes, functionalized polyolefins, polysulfones, polyethersulfones, and the like.

The functionalized PPE containing aliphatic unsaturation is especially useful in composite systems that involve a curing or polymerization step of unsaturated species, for example, styrene or acrylic-type monomers. It is believed that the aliphatic unsaturation introduced onto the PPE affords a reaction path to chemically link the PPE into composite system. Moreover, many of these same composite systems cure or polymerize, at least in part, through radical reactions. Uncapped PPE contains phenyl hydroxyl moieties that interfere with such radical reactions. In one embodiment, the functionalized PPE containing aliphatic unsaturation has the free hydroxyl groups “capped” reducing the interference. By “capped” is meant that at least about 80%, preferably at least about 90%, more preferably at least about 95% or more of the hydroxyl groups of the PPE have been reacted. It should be clear that the present invention also includes reaction products between the PPE containing aliphatic unsaturation and composite systems that involve a curing and/or polymerization step of unsaturated species. It should also be clear that the PPE containing aliphatic unsaturation is useful with a wide range of thermosetting resins, including but not limited to those selected from the group consisting of epoxy, phenolic, alkyds, polyester, polyimide, polyurethane, mineral filled silicone, bismaleimides, cyanate esters, vinyl, and benzocyclobutene resins and can react in a variety of pathways with such resins.

One embodiment is a process to prepare a polyphenylene ether resin containing aliphatic unsaturation, comprising: reacting a polyphenylene ether resin with an unsaturated compound in a solvent to form a solution containing a polyphenylene ether resin containing aliphatic unsaturation, wherein the unsaturated compound has the formula

wherein R¹ is an aliphatic or aromatic residue, n can vary from 0 to about 10, and wherein each of R², R³, and R⁴ are independently hydrogen, alkyl, or aryl, and wherein X is a residue of one of the formulae

wherein R⁷ is an aliphatic or aromatic residue, m can vary from 0 to about 10, and wherein each R⁸, R⁹, and R¹⁰ are independently hydrogen, alkyl, or aryl; and precipitating the polyphenylene ether containing aliphatic unsaturation from the solution by combining the solution with an antisolvent, wherein the antisolvent comprises a compound selected from alkanols having one to about ten carbon atoms, ketones having three to about ten carbon atoms, and alkanes having five to about ten carbon atoms, and mixtures thereof.

There is no particular limit on the antisolvent employed in the method. Suitable antisolvents include lower alkanols having one to about ten carbon atoms, such as methanol, and the like; ketones having three to about ten carbon atoms, such as acetone, methyl ethyl ketone, and the like; and alkanes having five to about ten carbon atoms, such as hexane; and the like; and combinations thereof. Preferred alkanols include those having two to about six carbon atoms, more preferably three to five carbon atoms. Particularly preferred antisolvents include isopropanol and isobutanol. Highly preferred antisolvents include isopropanol. In one embodiment, the antisolvent may, optionally, comprise about 0.1 to about 30 weight percent of a C₆-C₁₈ aromatic hydrocarbon. In one embodiment, the antisolvent may, optionally, comprise about 0.1 to about 10 weight percent of water. In one embodiment, the antisolvent comprises about 60 to 99.8 weight percent isopropanol, about 0.1 to about 30 weight percent toluene, and 0.1 to about 10 weight percent water.

In one embodiment, the solvent comprises an aromatic solvent such as benzene, toluene, ethylbenzene, xylene, or o-dichlorobenzene; or a halogenated alkane such as tetrachloromethane, trichloromethane, dichloromethane, or 1,2-dichloroethane; or a halogenated alkene such as trichloroethylene. In another embodiment that is particularly useful when the polyphenylene ether resin containing aliphatic unsaturation is subsequently used to prepare a thermoset composition, the solvent comprises an alkenyl aromatic monomer. Suitable alkenyl aromatic monomers include, for example, styrene, α-methylstyrene, 2-methylstyrene, 3-methylstyrene, 4-methylstyrene, 2-t-butylstyrene, 3-t-butylstyrene, 4-t-butylstyrene, 1,3-divinylbenzene, 1,4-divinylbenzene, 1,3-diisopropenylbenzene, 1,4-diisopropenylbenzene, styrenes having from 1 to 5 halogen substituents on the aromatic ring, and the like, and combinations thereof. Preferred alkenyl aromatic monomers include styrene and divinyl benzenes.

The solution may comprise about 1 to about 70 weight percent of the polyphenylene ether resin containing aliphatic unsaturation, based on the total weight of the solution. Within this range, the concentration of the polyphenylene ether resin containing aliphatic unsaturation is preferably at least about 10 weight percent, more preferably at least about 20 weight percent, still more preferably at least about 30 weight percent. Also within this range, the concentration of the polyphenylene ether resin containing aliphatic unsaturation is preferably up to about 50 weight percent, more preferably up to about 40 weight percent. The solution may comprise about 30 to about 99 weight percent of the solvent, based on the total weight of the solution. Within this range, the concentration of the solvent is preferably at least about 40 weight percent, more preferably at least about 50 weight percent, still more preferably at least about 60 weight percent. Also within this range, the concentration of the solvent is preferably up to about 90 weight percent, more preferably up to about 80 weight percent, still more preferably up to about 70 weight percent.

In one embodiment, the precipitation is conducted by adding the solution comprising the polyphenylene ether containing aliphatic unsaturation to the antisolvent. In another embodiment, the precipitation is conducted by adding the antisolvent to the solution comprising the polyphenylene ether containing aliphatic unsaturation.

The precipitation may be conducted by mixing the solution comprising the polyphenylene ether containing aliphatic unsaturation and the antisolvent in a weight ratio of about 1:20 to about 1:2. Within this range, the weight ratio is preferably at least about 1:10, more preferably at least about 1:5. Also within this range, the weight ratio is preferably up to about 1:3, more preferably up to about 1:4. There is no particular limitation on the temperatures of the solution and the antisolvent when they are combined. It is preferred that the temperature of the solution is sufficiently high to maintain dissolution of the polyphenylene ether containing aliphatic unsaturation. The temperature of the solution may therefore depend on variables including the identity of the solvent, the concentration of the polyphenylene ether containing aliphatic unsaturation, the chemical (monomer) composition of the polyphenylene ether containing aliphatic unsaturation, and the molecular weight of the polyphenylene ether containing aliphatic unsaturation. For example, when the solution is a toluene solution containing 37 weight percent of a methacrylate-capped poly(2,6-dimethyl-1,4-phenylene ether) having an intrinsic viscosity of about 0.12 dL/g, the solution temperature may preferably be about 20 to about 100° C., preferably about 30 to about 80° C., more preferably about 35 to about 50° C. Preferably the temperature of the solution is below the boiling point temperature of the antisolvent. The temperature of the antisolvent may depend on the identity of the antisolvent, the ratio of solution to antisolvent, and the temperature of the solution, as well as the variable discussed above for the solution temperature. For example, when the antisolvent is isopropanol and the solution is a 40° C. toluene solution containing 37 weight percent of a methacrylate-capped poly(2,6-dimethyl-1,4-phenylene ether) having an intrinsic viscosity of about 0.12 dL/g, the antisolvent temperature may be about 10 to about 80° C., preferably about 15 to about 60° C., more preferably about 20 to about 40° C.

One embodiment is a process to prepare a polyphenylene ether resin containing aliphatic unsaturation, wherein said process comprises: reacting a polyphenylene ether resin with an unsaturated compound in a solvent to form a solution containing a polyphenylene ether resin containing aliphatic unsaturation; wherein the polyphenylene ether comprises 2,6-dimethyl-1,4-phenylene ether units, 2,3,6-trimethyl-1,4-phenylene ether units, or a mixture thereof; and wherein the unsaturated compound has the formula

wherein R¹ is an aliphatic or aromatic residue, n can vary from 0 to about 10, and wherein each of R², R³, and R⁴ are independently hydrogen, alkyl, or aryl; and precipitating the polyphenylene ether containing aliphatic unsaturation from the solution by combining the solution with an antisolvent, wherein the antisolvent comprises an alkanol having one to about ten carbon atoms.

Another embodiment is a process to prepare a polyphenylene ether resin containing aliphatic unsaturation, wherein said process comprises: reacting a polyphenylene ether resin with an unsaturated compound in a solvent to form a solution containing a polyphenylene ether resin containing aliphatic unsaturation; wherein the polyphenylene ether comprises 2,6-dimethyl-1,4-phenylene ether units, 2,3,6-trimethyl-1,4-phenylene ether units, or a mixture thereof; and wherein the unsaturated compound is methacrylic anhydride; and precipitating the polyphenylene ether containing aliphatic unsaturation from the solution by combining the solution with an antisolvent, wherein the antisolvent comprises an alkanol having three to about five carbon atoms.

Preferably, the rate of combination of polymer solution and antisolvent is low relative to the rate of mixing. For example, when polymer solution is added to antisolvent in a lab-scale batch process, addition of antisolvent to polymer solution is preferably conducted over a period of about three to about 6 minutes. When the addition is conducted in a minute or less, the precipitate may agglomerate and formed a large mass instead of small particles. The large mass is more likely to occlude impurities, solvent, antisolvent and the like. Moreover, the handling and drying of the precipitate are facilitated by the smaller particles. It may therefore be preferred to mix the solution and the antisolvent under high shear conditions. For example, the solution and the antisolvent may be combined by mixing with a shear rate of about 500 to about 50,000 sec⁻¹.

One embodiment is a polyphenylene ether resin containing aliphatic unsaturation, prepared by any of the above precipitation methods. Compared to resins isolated by devolatilization, those isolated by precipitation contain lower levels of residual unsaturated compound. For example, the polyphenylene ether resin containing aliphatic unsaturation isolated by precipitation may comprise less than 100, preferably less than 50, more preferably less than 20, even more preferably less than 10, parts per million by weight of residual unsaturated compound.

In order that those skilled in the art will be better able to practice the invention, the following examples are given by way of illustration and not by way of limitation.

EXAMPLES

Polymerization Reaction

A typical laboratory reaction recipe and reaction conditions are provided.

The catalyst solution can be prepared by stirring 0.41 g of cuprous bromide and 10.9 g of di-n-butyl amine in 100 ml of toluene. The catalyst is transferred to a one liter stirred glass reactor equipped with an internal cooling coil and inlet tubes for oxygen and monomer. A rapid stream of oxygen is introduced near the bottom of the reactor and a solution of 70 g of 2,6-xylenol in 100 ml of toluene is added through a metering pump, over a period of fifteen minutes, to the rapidly stirred solution. The temperature is maintained initially at about 40° C. to about 45° C./48° C. towards the end of the run by circulating water from a constant temperature bath through the cooling coil. Molecular weight build is continuously monitored with a typical reaction time to target I.V. of about 100-107 minutes.

In the glass reactor vessel, the copper catalyst was complexed by the addition of a complexant like nitrilotriacetic acid (NTA) or other copper complexing agent in order to solubilize it in the aqueous liquid phase. The equilibration time was approximately 70 minutes and the temperature was approximately 55° C. The catalyst was removed with centrifugation.

Although the conditions are for a laboratory scale reaction they in general scaleable to commercial processes carried out in commercial equipment without undue burden by one of skill in the art.

General Procedure for Preparing PPE Containing Residual Aliphatic Unsaturation

In a dry 250 ml 3-neck round bottom flask was added a 40 weight percent solution of PPE in toluene amount and a “magnet” for stirring. The flask was placed in a oil bath, the temperature was set to the reaction temperature. A slow nitrogen purge was applied and maintained during the reaction. The catalyst 4-dimethylaminopyridine (DMAP) or 4-dimethylbutylamine (DMBA) was added. After 15 minutes, when the catalyst had dissolved, the reaction was started by adding the amount of methacrylic anhydride (MAA). After about 30 minutes, the toluene was removed with vacuum stepwise decreasing from atmospheric pressure to about 40 mm Hg. The sample was dried in a vacuum oven for about 10 hours at about 120° C./10 mm Hg, ground to powder form and dried for another 3 hours at 120° C./10 mm Hg. The capping conversion was determined on the totally isolated methacrylic-PPE (by-product as MAA, methacrylic acid and DMAP were not removed). The [OH] content is measured by FT-IR (carbon disulfide). The capping conversion is calculated by the formula: Conversion %=(A−B)/A×100%, A=[OH]PPE ref., B=[OH]Methacrylic-PPE sample.

TABLE 1 PPE MAA type OH for rx OH after rx Conv. (wt % Temp. (dl/g) (μmol/g) (μmol/g) (%) vs PPE) Catalyst (° C.) 0.12 344  23 93 5.0 DMAP 80 0.12 344  74 78 10.0 DMAP 80 0.12 344  75 78 5.0 DMAP 260  0.12 361 208 42 5.0 DMBA 80 0.12 361 124 66 10.0 DMBA 80 0.12 361 122 66 15.0 DMBA 80 0.12 400 204 49 5.0 DMBA 260  As can be seen by these data, very high conversion to the capped PPE containing aliphatic unsaturation can be readily achieved. Moreover, it was unexpectedly found that DMAP gave appreciably higher conversions that DMBA.

Designed Experimental

A series of designed experiments were conducted to further exemplify embodiments of the invention using the same general procedure. The results are shown in Table 2.

TABLE 2 [MAA] [DMAP] Conversion Run in wt % in wt % (%) 1 5.5 3 79 2 6 2 82 3 6 4 84 4 7 3 93 5 8 2 98 6 8 4 99 7 8.5 3 100

These reactions were conducted at 80° Celsius, for one hour, using 30 wt % PE in toluene, with a stirring speed of 300 rpm.

As can be seen by the data in Table 2, high conversion can be readily obtained under a wide variety of conditions illustrating the broad utility of the present invention.

Total Isolation

Functionalized PPE containing residual aliphatic unsaturation was also prepared and totally isolated.

Step 1: MAA capping of PP0857 in Toluene. Conditions: 40 wt % PPE in Toluene, 6.5 wt % MAA and 3 wt % DMAP; 90° C., 300 rpm stirring, 2 hours, Nitrogen; recipe 180.1 g Toluene, 112.7 g PPE, 8.1 g MAA, 3.4 g DMAP. After the reaction, a ca. 20 g sample was poured out on aluminum disk. The toluene was allowed to evaporate at room temperature. The material was ground and dried for about 8 hours at about 120° C./10 mm Hg. The material transferred to a “Parr-bomb”, see step 2.

Step 2: Methacrylic-PPE solution in toluene treatment at high temperatures and pressures. A 300 ml vessel for high temperature and high pressure, so-called Parr-bomb, was filled with solution of step 1. At 70° C., flush with nitrogen for about 5 minutes, then the vessel was closed. After 10 minutes at about 245° C., the pressure readout was about 45 bar. The temperature was maintained at about 245° C. for about 30 minutes, then cooled to about 80° C. over about 30 minutes. The solution was poured out on aluminum disks. The toluene was allowed to evaporate at room temperature. The material was ground and dried for about 8 hours at about 120° C./10 mm Hg, and used for step 3.

Step 3: Extrusion of Methacrylic-PPE in Prism twin (16 mm screws) extruder. An 80 g sample of totally isolated methacrylic-PPE was used; all by-products were present. Conditions: barrel temperatures from nozzle to throat were 257-283-276-250° C.; 250 rpm, 25% Torque (5 Nm). The extrudate was dried for about 8 hours at about 120° C./10 mm Hg, afterwards ground.

TABLE 3 Results MAA/PPE reaction for direct isolation % Conversion % double bonds direct isolation by FT-IR* by NMR** Step 1 Reaction in 92 83 toluene Step 2 Treatment high 92 Not determined temperature & pressure Step 3 Extrusion 90 Not determined *Total isolation, by-products are present **Extracted with ethanol to remove by-products

The data in Table 3 demonstrate that the residual unsaturation can, unexpectedly, substantially survive the direct isolation thermal conditions. FT-IR analysis done before and after extrusion had critical peak ratios that were essentially constant, indicating very little change in the amount of double bonds or capping.

Capping of PPE Pellets From Direct Isolation

A series of capping reactions were conducted using PPE that had been isolated by total isolation using devolatilization of the PPE polymerization solvent.

In a typical experiment, to 1000 ml 4-neck round bottom jacketed glass reactor (L/D=1.5) equipped with a 45° pitch four-blade agitator operating at 1000 rpm was added toluene (311 g) at 40° C. followed by PPE pellet (0.12 I.V., 133 g) and the system was purged with nitrogen gas. The reaction solution temperature was increased to 60° C. and 4-N,N′-dimethylaminopyridine (DMAP, 6.7 g, 5% wt based on PPE) was added. The resulting solution was heated to 85° C., and then methacrylic anhydride (MAA, 16 g, 12% wt based on PPE) was added. The solution was maintained at about 85° C. for about 30 to 400 minutes until the end capping reaction. At the end of reaction, the reaction solution was cooled, discharged from reactor, precipitated with 2 times volume of methanol, vacuum filtered with 100 mesh filtration cloth and vacuum dried for about 8 hours at 100° C. During reaction, every 30 minutes, about 1 ml reaction solution sample was taken and immediately dissolved into 25 ml carbon disulfide for testing of residual OH content. The [OH] content is measured by FT-IR (carbon disulfide). The capping conversion is calculated by the formula: Conversion %=(A−B)/A×100%, A=[OH]PPE ref., B=[OH]Methacrylic-PPE sample. The results of capping PPE pellets in solvent are listed in Table 4.

TABLE 4 Pre-Pilot capping reaction results Batch MAA % DMAP % % CAPPED Temp = 85° C. 1 8 2.75 82.6 2 8 0.5 81.0 3 12 5 99.4 4 8 5 89.7 5 12 0.5 98.5 6 8 2.75 82.6 7 10 2.75 98.9 8 12 5 100.0 9 12 2.75 99.4 Temp = 45° C. 10 12 2.75 99.4 The above examples demonstrate the high levels of capping that can be achieved using PPE that has been directly isolated by removal of the PPE polymerization solvent. It was unexpected that such a high degree of capping would be achieved without having to pre-wash the PPE solution to remove impurities from the polymerization reaction.

Large Scale Capping PPE Pellet In Solution

To illustrate the commercial feasibility of one embodiment of the invention, to a 300 gal 316 stainless steel reactor (L/D=1.1) equipped with two layer three blade propeller variable speed agitator (43 to 430 rpm) and a jacket and external circulation loop through a heat exchanger to control reaction temperature was added 250 lb. of low I.V. PPE (0.12 I.V.) pellets obtained from a total isolation of the PPE reaction solution using devolatilization equipment with 564 lbs of toluene at room temperature. To the reaction solution was added 6.9 lbs. (2.75% wt based on PPE) of 4-N,N′-dimethylaminopyridine (DMAP) and 25 lbs (10% wt based on PPE) of methacrylic anhydride (MAA). The reaction temperature was controlled to about 85° C. Essentially 100% OH conversion was achieved after about 150 minutes as detected by FT-IR analysis.

PPE Pellet Capping in Styrene

To a three-necked round bottom flask equipped with an overhead mechanical stirrer, a condenser, and a thermocouple was added styrene (200 mL), followed by PPE (0.12 I.V., 181.8 g) and 4-N,N′-dimethylaminopyridine (DMAP,1.22 g). The resultant solution was heated to about 85° C., and methacrylic anhydride (MAA, 21.8 g) was added. The solution was maintained at about 85° C. for about 8 hours to complete the reaction. The capping efficiency was found to be 98.5%. Table 5 is a summary of results.

TABLE 5 Lab Results of Capping Low IV PPE in Styrene Monomer Reaction Reaction Capping PPE Styrene DMAP MAA temp time efficiency (g) (mL) (g) (g) (° C.) (hrs) (%) 1 181.8 200 5 21.8 85 2 100.0 2 181.8 200 2.5 21.8 85 4 99.7 3 181.8 200 1.22 21.8 85 8 98.5 4 181.8 200 0.61 21.8 85 17  98.2 These results illustrate that very high PPE capping conversions can be achieved in the presence of a polymerizable monomer such as a vinyl aromatic material such as styrene monomer.

One unexpected advantage of capping PPE that has not been isolated is a reduction in color when used in many applications. For example, a 10 weight percent styrene solution of MAA capped 0.12 IV PPE made from direct capping reaction body feed had a ΔE of 56 as compared to a 10 weight percent styrene solution of MAA capped 0.12 IV PPE made from capping re-dissolved 0.12 IV PPE pellet in toluene had a ΔE of 66. This reduction in color is unexpected in view of the prior art in which one would expect the color to be very similar.

Isolation of Capped PPE by Precipitation

Methacrylate-capped poly(2,6-dimethyl-1,4-phenylene ether) resins were isolated by precipitations that varied in the identity of the antisolvent and the method of combining the polyphenylene ether solution with the antisolvent. The solution of 37 weight percent methacrylate-capped poly(2,6-dimethyl-1,4-phenylene ether) (intrinsic viscosity=0.12 dL/g) in chloroform was prepared by reaction of the corresponding uncapped polyphenylene ether (1406 g) with methacrylic anhydride (188.6 g) in toluene solvent (1406 g) with dimethylaminopyridine catalyst (17.9 g), as described above.

So-called “normal” precipitations, in which the toluene solution of capped polyphenylene ether was poured into the antisolvent, were conducted as follows. Four hundred milliliters of room temperature antisolvent (methanol, isopropanol, acetone, or methyl ethyl ketone (MEK)) were added to a WARING® blender equipped with a 1000 mL capacity glass container. While the antisolvent in the blender was agitated, a pre-weighed portion of approximately 140 grams of capped polyphenylene ether solution at about 40° C. was added drop-wise, causing precipitation of the capped polyphenylene ether. The resulting mixture was poured onto a PYREX® brand Büchner funnel with a coarse fritted disc, and a filter cake of the precipitated capped polyphenylene ether was allowed to form. Once a filter cake had formed, vacuum was applied to the filter to remove solvent. The precipitate was washed with an additional 50 mL of antisolvent, dried in an vacuum oven for 3.5 hours at 130° C., under 20 inches of vacuum with a flow of nitrogen at 15 standard cubic feet per hour. After removal from the oven and cooling to ambient temperature the material was weighed.

So-called “reverse” precipitations, in which the antisolvent was poured into the toluene solution of polyphenylene ether, were conducted as follows. A pre-weighed portion of approximately 140 grams of capped polyphenylene ether solution at about 40° C. was added to the blender. While the contents of the blender were agitated, 400 mL of antisolvent was added over the course of about six minutes, causing precipitation of the capped polyphenylene ether. The resulting precipitate was filtered, washed, and dried as described for the “normal” precipitation.

Each precipitated capped polyphenylene ether was characterized by determining its molecular weight and residual impurities. Number average molecular weight (M_(n)) and weight average molecular weight (M_(w)), each expressed in units of atomic mass units (AMU), were determined using GPC (gel permeation chromatography) using polystyrene standards. Residual concentrations of toluene, methacrylic acid, methacrylic anhydride, and dimethylaminopyridine, all expressed in parts per million by weight (ppm), were determined gas chromatography using a flame ionization detector. Residual concentrations of the antisolvents (methanol, isopropanol and acetone), all expressed in parts per million by weight (ppm), were determined by gas chromatography/mass spectrometry (GC/MS). Results are presented in Table 6. The results show that the reverse method yields lower levels of toluene and methacrylic acid, and higher levels of DMAP than the normal method. The normal method with isopropanol yields an exceedingly and unexpectedly low level of residual methacrylic anhydride. The normal precipitation with MEK selectively precipitates higher molecular weight capped polyphenylene ether, but this selectivity comes at the expense of yield.

TABLE 6 1 2 3 4 Precipitation Method normal normal normal normal Antisolvent methanol isopropanol acetone MEK Yield (%) 97.3 99.1 64.3 30.9 M_(n) (AMU) 2,822 3,051 4,345 6,144 M_(w) (AMU) 7,024 7,191 8,832 11,949 M_(n)/M_(w) 2.49 2.36 2.03 1.94 Toluene (ppm) 30,711 31,111 25,612 23,595 Methacrylic acid 7,524 6,365 9,595 8,467 (ppm) Methacrylic 57 5 50 850 anhydride (ppm) DMAP (ppm) 371 242 485 258 Methanol (ppm) ND — — — Isopropanol (ppm) — 19,846 — — Acetone (ppm) — — ND — ND = not detected (less than 10 ppm for methanol, 100 ppm for isopropanol, and 100 ppm for acetone) 5 6 7 Precipitation Method reverse reverse reverse Antisolvent methanol isopropanol acetone Yield (%) 97.7 98.2 70.3 M_(n) (AMU) 3,098.7 3,213.3 4,099.7 M_(w) (AMU) 7,172.7 7,202.3 8,769.7 M_(n)/M_(w) 2.31 2.24 2.14 Toluene (ppm) 4,174 4,418 38,358 Methacrylic acid 1,229 2,097 7,809 (ppm) Methacrylic 185 177 75 anhydride (ppm) DMAP (ppm) 738 504 522 Methanol (ppm) ND — — Isopropanol (ppm) — ND — Acetone (ppm) — — 352 ND = not detected (less than 10 ppm for methanol, and 100 ppm for isopropanol)

Isolation of Capped PPE by Devolatilization

A 50 weight percent solution of methacrylate-capped poly(2,6-dimethyl-1,4-phenylene ether) (intrinsic viscosity=1.2 dL/g) in toluene was prepared as described in the preceding example. Toluene was removed in a vacuum over under two conditions: (1) 200° C. for four hours, or (2) 100° C. for 2 hours. The non-volatile residue was analyzed to determine capped poly(arylene ether molecular weight and residual toluene, methacrylic acid, methacrylic anhydride, and DMAP. Results are presented in Table 7. The results show that there is a negligible effect on the molecular weight of the capped polyphenylene ether resins when isolated by devolatilization.

TABLE 7 1 2 M_(n) (AMU) 3,260 3,260 M_(w) (AMU) 7,240 7,240 M_(n)/M_(w) 2.20 2.20 Toluene (ppm) 1,179 28,405 Methacrylic acid (ppm) 1,322 23,167 Methacrylic anhydride (ppm) 930 668 DMAP (ppm) 68 88

Isolation of Capped PPE by Aqueous Washing Followed by Devolatilization

To reduce the amount of residual impurities, isolations were performed with a water wash prior to devolatilization. The solution of methacrylate-capped poly(2,6-dimethyl-1,4-phenylene ether) in toluene was warmed to a pre-determined temperature then mixed for 30 seconds by hand with an amount of warmed water. The mixture was centrifuged at 20,000 rpm for 2 minutes and the organic layer was recovered. The organic layer was dried for 4 hours at 120° C. in a vacuum oven. The resulting powders were analyzed for methacrylic acid, methacrylic anhydride, DMAP, and toluene. The washing conditions and results are shown in Table 8.

TABLE 8 Amt Meth- Meth- PPO in Mixing Water/ acrylic acrylic solution Temp. Organic acid anhydride DMAP Toluene (wt %) (° C.) Ratio (ppm) (ppm) (ppm) (ppm)  1 20 21 1 6909 208 321 53670  2 20 21 2 5978 189.5 304 54790  3 20 50 1 3310 465.5 220 21380  4 20 50 2 2668 297.5 195.5 19700  5 35 21 1 9254 293 163.5 48380  6 35 21 2 8739.5 423 144 57810  7 35 50 1 9133.5 453.5 113 50270  8 35 50 2 6627 432 110.5 53290  9 50 21 1 24990 345.5 35.5 59750 10 50 21 2 25003 358 33.5 55070 11 50 50 1 9211 329 91 56830 12 50 50 2 6680 284.5 96 53560 The results show that a higher polyphenylene ether concentration in solution, higher mixing temperature, and higher water/organic ratio each improve (decrease) the concentrations of residual compounds in the isolated polyphenylene ether resin. The water wash may, optionally, include acids, bases, or salts to facilitate extraction of impurities from the polyphenylene ether solution. For example, the water wash may contain sodium hydroxide at about 0.0001 to about 1 normal to facilitate extraction of methacrylic acid, and hydrolysis and extraction of methacrylic anhydride. As another example, the water wash may contain hydrochloric acid at 0.0001 to about 1 normal to facilitate extraction of dimethylaminopyridine. Efficient extraction of both basic and acidic impurities may be effected with sequential washes in acid and base, or vice versa. Furthermore, the aqueous extraction technique is useful as a pretreatment prior to precipitation, as well as prior to devolatilization.

While the invention has been described with reference to a preferred embodiment, it will be understood by those skilled in the art that various changes may be made and equivalents may be substituted for elements thereof without departing from the scope of the invention. In addition, many modifications may be made to adapt a particular situation or material to the teachings of the invention without departing from essential scope thereof. Therefore, it is intended that the invention not be limited to the particular embodiment disclosed as the best mode contemplated for carrying out this invention, but that the invention will include all embodiments falling within the scope of the appended claims.

All cited patents, patent applications, and other references are incorporated herein by reference in their entirety. 

1. A process to prepare a polyphenylene ether resin containing aliphatic unsaturation, wherein said process comprises: reacting a polyphenylene ether resin with an unsaturated compound in a solvent to form a solution containing a polyphenylene ether resin containing aliphatic unsaturation, wherein the unsaturated compound has the formula

wherein R¹ is an aliphatic or aromatic residue, n can vary from 0 to about 10, and wherein each of R², R³, and R⁴ are independently hydrogen, alkyl, or aryl, and wherein X is a residue of one of the formulae

wherein R⁷ is an aliphatic or aromatic residue, m can vary from 0 to about 10, and wherein each R⁸, R⁹, and R¹⁰ are independently hydrogen, alkyl, or aryl; and precipitating the polyphenylene ether containing aliphatic unsaturation from the solution by combining the solution with an antisolvent, wherein the antisolvent comprises a compound selected from alkanols having one to about ten carbon atoms, ketones having three to about ten carbon atoms, and alkanes having five to about ten carbon atoms, and mixtures thereof.
 2. The process of claim 1, wherein the polyphenylene ether containing aliphatic unsaturation has the formula

wherein R¹ is an aliphatic or aromatic residue; n is 0 to about 10; each of R², R³, and R⁴ is independently hydrogen, alkyl, or aryl; j has an average value less than 49; each Q¹ is independently halogen, primary or secondary lower alkyl, phenyl, haloalkyl, aminoalkyl, hydrocarbonoxy, or halohydrocarbonoxy wherein at least two carbon atoms separate the halogen and oxygen atoms; and each Q² is independently hydrogen, halogen, primary or secondary lower alkyl, phenyl, haloalkyl, hydrocarbonoxy or halohydrocarbonoxy wherein at least two carbon atoms separate the halogen and oxygen atoms.
 3. The process of claim 2, wherein j has an average value less than
 34. 4. The process of claim 2, wherein each Q¹ is methyl, and each Q² is hydrogen.
 5. The process of claim 1, wherein the polyphenylene ether resin comprises 2,6-dimethyl-1,4-phenylene ether units and 2,3,6-trimethyl-1,4-phenylene ether units.
 6. The process of claim 1, wherein n is
 0. 7. The process of claim 1, wherein the polyphenylene ether resin has an intrinsic viscosity of about 0.08 to about 0.25 dl/g as measured in chloroform at 25° C.
 8. The process of claim 1, wherein the unsaturated compound is acrylic anhydride, methacrylic anhydride, or a mixture thereof.
 9. The process of claim 1, wherein the solvent is selected from benzene, toluene, ethylbenzene, xylene, o-dichlorobenzene, tetrachloromethane, trichloromethane, 1,2-dichloroethane, and trichloroethylene.
 10. The process of claim 1, wherein the solvent comprises toluene.
 11. The process of claim 1, wherein the solvent is selected from styrene, α-methylstyrene, 2-methylstyrene, 3-methylstyrene, 4-methylstyrene, 2-t-butylstyrene, 3-t-butylstyrene, 4-t-butylstyrene, 1,3-divinylbenzene, 1,4-divinylbenzene, 1,3-diisopropenylbenzene, 1,4-diisopropenylbenzene, styrenes having from 1 to 5 halogen substituents on the aromatic ring, and combinations thereof.
 12. The process of claim 1, wherein the solvent comprises styrene.
 13. The process of claim 1, wherein the antisolvent comprises methanol, ethanol, n-propanol, isopropanol, n-butanol, isobutanol, acetone, methyl ethyl ketone, or a mixture thereof.
 14. The process of claim 1, wherein the antisolvent comprises an alkanol having two to six carbon atoms.
 15. The process of claim 1, wherein the antisolvent comprises an alkanol having three to five carbon atoms.
 16. The process of claim 1 wherein the antisolvent further comprises about 0.1 to about 30 weight percent of a C₆-C¹⁸ aromatic hydrocarbon.
 17. The process of claim 1 wherein the antisolvent further comprises about 0.1 to about 10 weight percent of water.
 18. The process of claim 1, wherein combining the solution with the antisolvent comprises adding the solution to the antisolvent.
 19. The process of claim 1, wherein combining the solution with the antisolvent comprises adding the antisolvent to the solution.
 20. The process of claim 1, wherein combining the solution with the antisolvent comprises mixing the solution and the antisolvent with a shear rate of about 500 sec⁻¹ to about 50,000 sec⁻¹.
 21. The process of claim 1, further comprising washing the solution with an aqueous solution prior to combining the solution with the antisolvent.
 22. A process to prepare a polyphenylene ether resin containing aliphatic unsaturation, wherein said process comprises: reacting a polyphenylene ether resin with an unsaturated compound in a solvent to form a solution containing a polyphenylene ether resin containing aliphatic unsaturation; wherein the polyphenylene ether comprises 2,6-dimethyl-1,4-phenylene ether units, 2,3,6-trimethyl-1,4-phenylene ether units, or a mixture thereof; and wherein the unsaturated compound has the formula

wherein R¹ is an aliphatic or aromatic residue, n can vary from 0 to about 10 and wherein each of R², R³, and R⁴ are independently hydrogen, alkyl, or aryl; and precipitating the polyphenylene ether containing aliphatic unsaturation from the solution by combining the solution with an antisolvent, wherein the antisolvent comprises an alkanol having one to about ten carbon atoms.
 23. A process to prepare a polyphenylene ether resin containing aliphatic unsaturation, wherein said process comprises: reacting a polyphenylene ether resin with an unsaturated compound in a solvent to form a solution containing a polyphenylene ether resin containing aliphatic unsaturation; wherein the polyphenylene ether comprises 2,6-dimethyl1,4-phenylene ether units, 2,3,6-trimethyl-1,4-phenylene ether units, or a mixture thereof; and wherein the unsaturated compound is methacrylic anhydride; and precipitating the polyphenylene ether containing aliphatic unsaturation from the solution by combining the solution with an antisolvent, wherein the antisolvent comprises an alkanol having three to five carbon atoms.
 24. A polyphenylene ether resin containing aliphatic unsaturation, prepared according to the method of claim
 1. 25. The polyphenylene ether resin containing aliphatic unsaturation of claim 24, comprising less than 100parts per million by weight of residual unsaturated compound.
 26. A polyphenylene ether resin containing aliphatic unsaturation, prepared according to the method of claim
 22. 27. The polyphenylene ether resin containing aliphatic unsaturation of claim 26, comprising less than 100parts per million by weight of residual unsaturated compound.
 28. A polyphenylene ether resin containing aliphatic unsaturation, prepared according to the method of claim
 23. 29. The polyphenylene ether resin containing aliphatic unsaturation of claim 28, comprising less than 100 parts per million by weight of residual unsaturated compound. 